General Information of Magnesia Chrome Brick MGe8
CMAX magnesia chrome bricks MGe8 use the sintered magnesium and chromite as the raw materials. Due to there are many impurities, the refractory grain are silicate bonded. The magnesia bricks are produced by crushing, mixing, pressing, drying and burning. The magnesia bricks are belong to alkali series refractories and widely used in alkaline atmosphere. A variety of type could be done according to customer’s request.
Characteristics of Magnesia Brick MGe8
Our magnesia bricks MZ87 exhibit the following characteristics:
Strong resistance to slag
Good high temperature properties
Typical Application of Magnesia Brick MGe8
Silicate Bonded Magnesia Chrome Brick---MGe-8 | ||||
| MGe-8A | MGe-8B | MGe-8C | |
Physical Properties: |
|
|
|
|
Cold Crushing Strength | Mpa | 40 | 35 | 30 |
Apparent Porosity | % | 18 | 19 | 21 |
Refractories Under Load(0.2Mpa) | ℃ | 1700 | 1650 | 1530 |
Chemical Analysis: |
|
|
|
|
MgO | % | 70.0 | 65.0 | 60.0 |
Cr2O3 | % | 8.0 | 8.0 | 8.0 |
Note: | ||||
Typical applications of magnesia bricks include ferroalloy furnace, metal mixer, Non-metallurgy industry furnace, calcined lime furnace, regenerator in glass furnace, high temperature kiln.
CNBM has success in magnesia bricks due to their cost-effectiveness, excellent thermal shock resistant and high temperature properties. CNBM also has experience in magnesia brick application and would like to assist you in product selection, system design, and installation techniques.