Hot blast stove refractory brick

Aug 22, 2023

Specifications

Fire brick
1.ISO 9001 approved,
2.With high quality and competitive price,
3.Standard and special shape.

Fire-clay refractory brick.
1. N-1
AL2O3 (%)>42
Refractoriness >1750
Refractoriness under load KD>1400
Permanent linear change onreheating
1500*2h
1450*2h
1400*2h:+0.1; -0.4
Apparent Porosity(%)<22
Cold crushing strength (Mpa)>29.4

2. N-2a
AL2O3 (%)>40
Refractoriness >1730
Refractoriness under load KD>1350
Permanent linear change onreheating
1500*2h
1450*2h
1400*2h:+0.1; -0.5
Apparent Porosity(%)<24
Cold crushing strength (Mpa)>24.5

High-alumina refractory brick
1. LZ-75
AL2O3 (%)>75
Refractoriness>1790
Refractoriness under load KD>1520
Permanent linear change onreheating
1500*2h:+0.1; -0.4
1450*2h
1400*2h
Apparent Porosity(%)<23
Cold crushing strength (Mpa)>53.9

2. LZ-65
AL2O3 (%)>65
Refractoriness >1790
Refractoriness under load KD>1500
Permanent linear change onreheating
1500*2h:+0.1; -0.4
1450*2h
1400*2h
Apparent Porosity(%)<23
Cold crushing strength (Mpa)>49

3.LZ-55
AL2O3 (%)>55
Refractoriness >1770
Refractoriness under load KD>1470
Permanent linear change onreheating
1500*2h:+0.1; -0.4
1450*2h
1400*2h
Apparent Porosity(%)<22
Cold crushing strength (Mpa)>44.1

4.LZ-48
AL2O3 (%)>48
Refractoriness >1750
Refractoriness under load KD>1420
Permanent linear change onreheating
1500*2h
1450*2h:+0.1; -0.4
1400*2h
Apparent Porosity(%)<22
Cold crushing strength (Mpa)>39.2

Fire clay brick SK-32
Item	Standard
AI2O3(%)	30
Fe2O3 (%)	3.5
Refractoriness (SK)	32
Refractoriness under load, 0.2MPa, Ta, (°C)	1300
Porosity (%)	22-26
Bulk density (g/cm³)	2.05
Cold crushing strength (MPa)	25
Thermal expansion at 1000°C (%)	0.6

Fire clay brick SK-34
Item	Standard
AI2O3(%)	38
Fe2O3 (%)	2.5
Refractoriness (SK)	34
Refractoriness under load, 0.2MPa, Ta, (°C)	1350
Porosity (%)	19-23
Bulk density (g/cm³)	2.10-2.15
Cold crushing strength (MPa)	25
Thermal expansion at 1000°C (%)	0.6

Fire clay brick SK-36
Item	Standard
AI2O3(%)	50
Fe2O3 (%)	2
Refractoriness (SK)	36
Refractoriness under load, 0.2MPa, Ta, (°C)	1450
Porosity (%)	20-24
Bulk density (g/cm³)	2.30-2.40
Cold crushing strength (MPa)	45
Thermal expansion at 1000°C (%)	0.3