Quick Details
| Application: | Heat Insulation | Thickness: | 20-150mm | Width: | 600mm |
| Length: | 900-1000mm | Grade: | HA (High Aluminum) | Chemical Composition: | Al2O3+SiO2=99.8% |
| Ultimate Strength (≥ MPa): | Ceramic Fiber Board | Working Temperature: | 1000C, 1200C, 1300C, 1500C, 1700C | Fiber Diameter: | Ceramic Fiber Board |
| Thermal Conductivity: | Ceramic Fiber Board | Shrinkage (1800℉, 3h): | <1% | Place of Origin: | China (Mainland) |
| Model Number: | MSCF | Brand Name: | Color: | White |
Packaging & Delivery
| Packaging Detail: | Ceramic Fiber Board Package is Wood box paded with foam |
| Delivery Detail: | 1-3 WEEKS |
Specifications
1. High quality ceramic fiber board.
2. High working tmperature.
3. Fast delivery and very competitive prices.
Ceramic Fiber Board is our main product.Mission can make high quality alumina fiber blanks and blanket. They are widely used as furnace lining in all kinds high temperature furnace and kiln. And also used for other high temperature resistance application.
Temperature and technical data of Mission alumina fiber board.
Type | MSCF-1000 | MSCF-1260 | MSCF-1400 | MSCF-1600 | MSCF-1800 | |
Temperature°C | 1000°C | 1260°C | 1400°C | 1600°C | 1800°C | |
Density(Kg/m3) | 300-600 | 300-600 | 300-600 | 450 | 550 | |
Chemical Components | Al2O3 | 38 | 42 | 50 | 68 | 85 |
Al2O3+SiO2 | 96.0 | 98 | 99 | 99.5 | 99.8 | |
Fe2O3 | 0.2 | 0.2 | 0.2 | ~ | ~ | |
Standard Sizes of Mission Alumina Fiber Board
900x600x(20-150)mm 1000x600x(20-150)mm
Other shapes and Sizes can be made according to your requirements!
Features of Mission Alumina Fiber Board.
1. Good High temperature stability, Low thermal conductivity,
2. Good thermal shock resistance, Corrosion resistance
3. Easy to be machined and cut. Precise thickness and sizes.
4. Good resistance of fire and high temperature gases.
5. Esy to installed.
6. Special shapes can be made.
Application of Mission Alumina Fiber Board.
Furnace lining and backing of various high temperature furnace and kiln.
Other high temperature appliation