General Information of High Alumina Brick 92%
Our company’s High Alumina Bricks are the final result of blending excellent high-purity fused alumina as the main rawmaterial with cutting-edge technology, adding superfine powder, after mixing, drying, forming, in the high temperature shuttle kiln. We make sure that the High Alumina Bricks offered by us have gone through all the quality control parameters for maintaining their high quality standard. Their durability and strength adds life to the structure and they possess the capacity of bearing high temperature.
Technical Data of High Alumina Brick 92% | ||
Physical Properties: |
|
|
Refractoriness | ℃ | 1850 |
Permanent Linear Change(1600℃×2h)% | % | ±0.1 |
Apparent Porosity, % | % | ≤18 |
Cold Crushing Strength | Mpa | ≥80 |
Refractoriness Under Load (T0.6) | ℃ | ≥1700 |
Thermal Expansion, % | % | ≤0.8 |
Density | g/cm3 | ≥3.0 |
Chemical Analysis: |
|
|
Al2O3 | % | ≥92 |
Fe2O3 | % | ≤0.8 |
Note:
Technical Data are typical average results from test pieces. The technical data is offered solely for your consideration. And CNBM reserve the right to modify the technical data without any prior notice. Users of CNBM products should make their own tests to determine the suitability of each product for their particular purposes.
| ||
Feature of High Alumina Brick 92%
Good thermal shock resistance
Low porosity
Good erosion resistance
High compressive strength
Excellent high temperature mechanics
Application of High Alumina Brick 92%
High Alumina Bricks are mainly used:
1). As lining components for the high temperature industries furnace (such as refractory, electronics, ceramics industries).
2). As Thermal insulation components for the high temperature heating equipments, such as gas making furnace, gasification furnace of petrochemical industry, reacting furnace of off-colour industry, electric induction furnace of metallurgical industry.